Weight-loss and surface roughness of enamel after microabrasion procedure with different agents / Perda de peso e rugosidade da superfície do esmalte após procedimento de microabrasão com diferentes agentes

Introduction: Enamel microabrasion is achieved by abrasion of the enamel surface and it is a quick, practical and efficient procedure. Objective It was assessed the weight loss and surface aspect of enamel after microabrasion procedures with commercial and mixtures made in-office. Material and method Eighty bovine incisors were divided into four groups (n=10): OpalustreTM (6.6% HCl + silicon carbide); Whiteness RMTM (6% HCl + silicon carbide); 37% H3PO4 + pumice and 10% HCl + pumice. Treatment was performed by 15 applications of 10s duration. The enamel weight loss was determined by the difference in weight before and after the microabrasion. The surfaces were analyzed by a surface roughness equipment and scanning electron microscopy. Data were submitted to paired-T test, one-way ANOVA and Tukey tests (α=0.05). Result It was observed significantly weight loss for all groups. The difference in weight loss ranged from 0.037±0.012 for group 37% H3PO4 and from 0.054±0.009 for group 6,6% HCl. There was a significant increase in surface roughness for all groups and 10% HCl group showed the lower results (0.65±0.09). It was observed different patterns of enamel morphology by SEM images. Conclusion The in-office mixtures resulted in the lowest enamel structure loss (37% H3PO4) and the lowest surface roughness (10% HCl).

Introdução: A microabrasão do esmalte é realizada através da abrasão da superfície do mesmo, apresentando-se como um procedimento rápido, prático e eficiente. Objetivo Avaliar a perda de peso e o aspecto superficial do esmalte após procedimentos de microabrasão com agentes comerciais e não comerciais. Material e método Oitenta incisivos bovinos foram divididos em quatro grupos (n = 10): OpalustreTM (6,6% HCl + carboneto de silício); Whiteness RMTM (6% HCl + carboneto de silício); 37% H3PO4 + pedra-pomes e 10% HCl + pedra-pomes. O tratamento foi realizado em 15 aplicações de 10s de duração. A perda de peso do esmalte foi determinada pela diferença de peso antes e depois da microabrasão. As superfícies foram analisadas por equipamento de rugosidade superficial e microscopia eletrônica de varredura. Os dados foram submetidos ao teste T-pareado, ANOVA one-way e teste de Tukey (α = 0,05). Resultado Foi observada perda de peso significativa para todos os grupos, a diferença na perda de peso variou de -0,037±0,012 para o grupo 37% H3PO4 a -0.054±0.009 para o grupo 6.6% HCl. Houve um aumento significativo na rugosidade da superfície para todos os grupos e o grupo 10%HCl apresentou os resultados mais baixos (0,65±0,09). Foram observados diferentes padrões de morfologia do esmalte por meio de imagens MEV. Conclusão Os agentes não comerciais resultaram na menor perda de estrutura do esmalte (37% H3PO4) e na rugosidade superficial (10% HCl).

Effect of SiO2 and Al2 O3 nanoparticles on wear resistance of PMMA acrylic denture teeth / Efeito das nanopartículas de SiO2 e Al2 O3 na resistência ao desgaste de dentes em acrílico PMMA para prótese

Objetivo: Este estudo teve como objetivo avaliar a resistência ao desgaste de dentes em acrílico para próteses contendo nanopartículas de dióxido de silício (nano-SiO2 ) e dióxido de alumínio (nanoAl2 O3 ). Material e Métodos: O material em polimetilmetacrilato (PMMA) foi utilizado para fabricar 84 amostras (n=10) contendo nano-SiO2 e nano-Al2 O3 nas concentrações 0,1% em peso, 0,3% em peso e 0,5% em peso de pó acrílico. Uma máquina de teste de desgaste de dois corpos e um microscópio digital foram usados para medir as mudanças na perda de peso e rugosidade da superfície, respectivamente. Testes de ANOVA a um fator e testes de comparações múltiplas de Tukey foram utilizados para análise dos dados (α = 0,05). Resultados: O material modificado com nano-SiO2 demonstrou um aumento significativo na perda de peso em comparação com o material acrílico artificial convencional (p ˂ 0,05) enquanto o material modificado com nano-Al2 O3 demonstrou aumento não significativo na perda de peso, exceto no subgrupo 0,5% (p < 0,05). Não há diferenças significativas em relação à alteração da rugosidade após a simulação de desgaste entre todos os grupos testados (p > 0,05). Conclusão: As nanopartículas de nano-Al2 O3 exibem menos efeito negativo que o nanoSiO2 , podendo ser usado com cautela, se necessário. (AU)

Objective: This study aimed to evaluate the wear resistance of acrylic denture teeth containing silicon dioxide (nano-SiO2 ) and aluminum dioxide (nano-Al2 O3 ) nanoparticles. Material and Methods: Poly methyl methacrylate (PMMA) denture tooth material was used to denture tooth material was used to fabricate 84 specimens (n=10) containing nano-SiO2 and nano-Al2 O3 in concentrations 0.1wt%, 0.3wt%, and 0.5wt% of acrylic powder. A two-body wear testing machine and digital microscope were used to measure the changes in weight loss and surface roughness respectively. One-way ANOVA and pair-wise Tukey's post-hoc tests were used for data analysis (α = 0.05). Results: Nano-SiO2 modified teeth material demonstrated a significant increase in weight loss in comparison conventional artificial acrylic teeth material (p ˂ 0.05) while nanoAl2 O3 modified teeth material demonstrated non-significant increase in weight loss except for 0.5% subgroup (p ˂ 0.05). There is no significant differences regarding roughness change after wear simulation among all tested groups (p > 0.05). Conclusion: Nano-Al2 O3 nanoparticles exhibit less negative effect than nano-SiO2 so; it could be used with caution if necessary. (AU)

Effect of different bleaching agents on the surface roughness and color stability of feldspathic porcelain / Efeito de diferentes agentes de clareamento na rugosidade superficial e estabilidade de cor da porcelana feldspática

Objective: The aim of this study was to evaluate the effect of different bleaching agents on the surface roughness and color stability of feldspathic porcelain. Material and Methods: In this study, totally 40 discshaped Noritake and Ceramco 3 feldspathic porcelain and two bleaching agents (Opalescence Boost and Opalescence Pf) were used. Bleaching agents were exposed to specimens according to their protocol. Then, the surface roughness of the specimens was evaluated with profilometer and the color of the specimens was recorded by colorimeter. Statistical analysis of the data was performed with IBM SPSS Statistics 20. Results: The results showed that that there were statistically significant differences between the bleaching agents on the surface roughness of feldspathic porcelain (p0.05). Conclusion: The obtained data presented that the bleaching agents increased the surface roughness and not affect the color stability of the feldspathic porcelain. (AU)

Objetivo: O objetivo deste estudo foi avaliar o efeito de diferentes agentes clareadores sobre a rugosidade superficial e estabilidade de cor da porcelana feldspática. Material e Métodos: Neste estudo, foram utilizados 40 porcelanas feldspáticas Noritake e Ceramco 3, em forma de disco, e dois agentes clareadores (Opalescence Boost e Opalescence Pf). Os agentes clareadores foram expostos às amostras de acordo com seu protocolo. Em seguida, a rugosidade superficial dos corpos de prova foi avaliada com perfilômetro e a cor dos corpos de prova foi registrada por colorímetro. A análise estatística dos dados foi realizada com o IBM SPSS Statistics 20. Resultados: Os resultados mostraram que houveram diferenças estatisticamente significantes entre os agentes clareadores na rugosidade superficial da porcelana feldspática (p 0,05). Conclusão: Os dados obtidos mostraram que os agentes clareadores aumentaram a rugosidade superficial e não afetaram a estabilidade de cor da porcelana feldspática.(AU)